Microstructure of melt-processed Bi2Sr2CaCu2Oy and reaction mechanisms during post heat treatment
| Author | Heeb, B.; Oesch, S.; Bohac, P.; Gauckler, L.J. | |
| Year | 1992 | |
| Type | Journal Article | |
| Journal | J. Mater. Res. | |
| Volume | 7 | |
| Issue | 11 | |
| Pages | 2948-2955 | |
| Date | 1992/11 | |
| Custom 1 | JA | |
| Custom 2 | SUPRA | |
| Abstract | Phase compositions and microstructures of melt processed 2212 were studied. 2212 starting powder was cooled from temperatures between 910[deg]C and 1100[deg]C in air at rates ranging from 350 K/min to 0.083 K/min. The solidification sequence was established for all cooling rates. Under all conditions the Bi-free (Sr, Ca)CuO2 (01 x 1) is the primary phase. The one-layer solid solution 11905 nuclates on this phase. The residual liquid solidifies to a glassy state, decomposes into the eutectic of Cu2O and Bi2Sr2.1Ca0.9Ox, or reacts with the primary phase and the 11905 forming 2212 at high, intermediate, or low cooling rates, respectively. Post solidification heat treatment at 850[deg]C in air leads to partial remelting. The Cu-rich liquid reacts with 11905 and 01 x 1 forming 2212. Subsequent solid/solid reactions lead to a high volume fraction of 2212 with almost ideal 2:2:1:2 stoichiometry. [Author abstract; 27 Refs; In English] | |
| URL | ||
| Record Number | 93 | |
| Group | nonmet |
Wichtiger Hinweis:
Diese Website wird in älteren Versionen von Netscape ohne
graphische Elemente dargestellt. Die Funktionalität der
Website ist aber trotzdem gewährleistet. Wenn Sie diese
Website regelmässig benutzen, empfehlen wir Ihnen, auf
Ihrem Computer einen aktuellen Browser zu installieren. Weitere
Informationen finden Sie auf
folgender
Seite.
Important Note:
The content in this site is accessible to any browser or
Internet device, however, some graphics will display correctly
only in the newer versions of Netscape. To get the most out of
our site we suggest you upgrade to a newer browser.
More
information
!!! Dieses Dokument stammt aus dem ETH Web-Archiv und wird nicht mehr gepflegt !!!
!!! This document is stored in the ETH Web archive and is no longer maintained !!!
!!! This document is stored in the ETH Web archive and is no longer maintained !!!