Experimental Phase Diagram Determination and Thermodynamic Assessment of the CeO2-Gd2O3-CoO System
Author |
|
Ivas, T.; Povoden-Karadeniz, E.; Grundy, N.; Jud-Sierra, E.; Grasslin, J.; Gauckler, L. J. |
Year |
|
2013 |
Type
|
|
Journal Article |
Journal |
|
Journal of the American Ceramic Society |
Volume |
|
96 |
Issue |
|
2 |
Pages |
|
613-626 |
Date |
|
Feb |
ISSN |
|
0002-7820 |
Accession Numer |
|
WOS:000314922200048 |
Abstract |
|
New phase diagram data and a thermodynamic assessment of the CeO-Gd2O3-CoO system using the CALPHAD approach are presented. This information is needed to understand the surprisingly low sintering temperature (950 degrees C1050 degrees C) of CeO2-based materials doped with small amounts of transition metal oxide (e.g., CoO). Experimental phase equilibria between 1100 degrees C and 1300 degrees C are reported based on the analysis of annealed and molten samples. No isolated compound exists in the ternary. At 1300 degrees C the Co solubility in the ternary compounds Ce1xyGdxCoyO2x/2y (fluorite) is 2.7mol% and is less than 1mol% in the Gd2xCexO3+x/2 (bixbyite). The Ce solubility in the perovskite GdCoO3 was found to be 1mol%. The lowest temperature eutectic melt in the ternary has a composition of 57.2mol% Co and 41.1mol% Gd melting at an onset temperature of 1303 +/- 5 degrees C, which is close to the binary eutectic in the Gd2O3-CoO system at 60 +/- 2mol% Co and 1348 +/- 1 degrees C. |
Notes |
|
Ivas, Toni Povoden-Karadeniz, Erwin Grundy, Nicholas Jud-Sierra, Eva Graesslin, Jurgen Gauckler, Ludwig J. |
URL |
|
Access publication [Website]
Access publication [Website]
|
Link to PDF |
|
|
Record Number |
|
8 |
Group
|
|
nonmet |
Back to List
Wichtiger Hinweis:
Diese Website wird in älteren Versionen von Netscape ohne
graphische Elemente dargestellt. Die Funktionalität der
Website ist aber trotzdem gewährleistet. Wenn Sie diese
Website regelmässig benutzen, empfehlen wir Ihnen, auf
Ihrem Computer einen aktuellen Browser zu installieren. Weitere
Informationen finden Sie auf
folgender
Seite.
Important Note:
The content in this site is accessible to any browser or
Internet device, however, some graphics will display correctly
only in the newer versions of Netscape. To get the most out of
our site we suggest you upgrade to a newer browser.
More
information